| | Highly elastomeric two component putty based on acrylic emulsion resin and powder | | |
| • For filling hairline cracks, blow holes, voids, and surface discontinuities in concrete surfaces and also for binding both new and old concrete elements.
• Also to provide a highly flexible and adherent waterproof layer suitable to be applied on both new and old concrete substrates, masonry roofs, facades, balconies, and underground surfaces affected by constant damp.
• STOP200 Flex provides the treated substrates a highly flexible waterproof layer that is suitable for potable water storage tanks, reservoirs, towers, water retaining structures, swimming-pools, sewage treatment plants, and water channels.
Notes:
1- If higher mechanical properties are required it is recommended to use STOP200.
2- If a fast setting repair mortar is required it is recommended to use STOP200 Extra.
3- If a highly flexible waterproof coating suitable to be applied in high coat thicknesses is required it is recommended to use Flexcoat. | | |
| • Excellent flexibility, suitable to be applied in excessively high thickness without crack formation.
• Excellent for crack treatment in low temperatures and where a superior flexibility is required.
• Excellent adhesion on concrete, asbestos, tiles, etc….
• Provides protection from corrosion of reinforcement, as it prevents penetration of carbon dioxide and chlorides into the substrate.
• Non toxic, suitable for use on potable water storage tanks, reservoirs, towers, etc….
• Allows water vapor to escape from the structure, the concrete will be able to breathe.
• Excellent resistance to the effects of ultra-violet light, weathering and atmospheric pollution.
• Can be applied to areas subjected to light foot traffic (2mm thickness at least).
• Suitable for use on concrete surfaces affected by constant damp.
• Superior freeze / thaw resistance. | | |
| | • Method of Application : | Brush, floor trowel, or wide bladed putty knife. | | • Mixing Ratio : | (by weight):
-Brush:/Powder:5/Water:1/Resin:0.8
-Trowel:/Powder:5/Water:0.6/Resin:0.8 | | • Mixing : | Add the desired amount of fresh water, according to the method of application, into component A (powder) and mix thoroughly using a slow speed mixer. Then add the entire contents of component B (resin) (0.8 litre) slowly from the plastic bottle into the mixture and mix slowly in order to ensure that a uniform consistency is achieved. | | • Pot life : | 1 hour (higher temperatures will shorten the potlife sharply). | | • Thinner / Cleaner : | Clean applying tools immediately after application is completed by water. | | • Application Temperature : | 5-40?C. | | • Note : | When recoating, a special attention should be given toward drying time. |
| | |
| | • Color : | White. | | • Volume Solids : | (mixed)80 % (ASTM-D2697). | | • VOC : | 0 g/L (ASTM-D3960). | | • Flexibility : | Excellent. | | • Adhesion : | Very good. | | • Recommended film thickness : | 0.5-1 mm (brush) and 1-2 mm (trowel). | | • Theoretical spreading rate : | 1.6 m²/L at 0.5 mm “dry”. | | • Specific gravity : | 1.40 kg/L. | | • Water resistance : | Excellent. | | • Abrasian Resistance : | Excellent. | | • Number of Coats : | 2, allow 10-15 minutes interval prior to applying the second coat. | | • Packaging : | Component A (powder):5 Kg in paper bag
Component B (resin):0.8 Kg in plastic bottle |
| | |
| Coating performance is, in general, proportional to the degree of surface preparation. Surface must be clean, undamaged and free of oil, grease, and other contaminants prior to coating.
Remove fins, protrusions, and other loose material with a scrapper, sandpaper, or wire brush.
For best results, surfaces should be damp but not wet prior to applying STOP 200 Flex. Protect fresh applications from rain, strong wind and intense sun light for 12 hours | | |
| | • Note : | 24 hours, and 3 days prior to a continuous exposure to water. Drying time can be affected by many factors such as temperature, ventilation and coat thickness. Higher temperatures will shorten the drying times. Apply the second coat within 10-15 minutes, depending on temperature and relative humidity, otherwise de-bonding of the second coat could result. |
| | |
| • Store component A (powder) in dry conditions in the original and unopened paper bags. Avoid powder to be exposed to high temperatures and high humidity conditions. Component B (resin) must not be allowed to come into contact with metals that are likely to corrode. Containers must be kept tightly closed. Exposure to strong heat and frost must be avoided.
• Shelf life is two years from packing date in unopened original containers at 10 to 40°C. Containers should be kept tightly closed.
• Safety:
Avoid skin or eye contact. Prolonged contact may cause irritation of the skin and mucous membranes. | |
|
|
|
|
information in this data sheet and in all our data sheets are given to the best
of our knowledge based on laboratory testing and practical experience. Final results
depend on following instructions and on consumer skill. Our responsibility is limited
to providing products that Conform to samples and specimens provided by us. Due
to technical needs, we reserve the right to change any given specification without
notice.
|
|
|